Mango ABS 1.75mm 3D Printing Filament 1kg - White is a high quality filament with 1.75mm diameter and 1kg Spool. This Filaments are Made In India with high quality processing and to promote Indian technology.
ABS stands for Acrylonitrile Butadiene Styrene. ABS is a dimensionally stable and impact resistant. It has a high tensile strength and good overall toughness. ABS is the same material that Lego bricks are made out of and is a great plastic for working parts. Final products made with ABS are very durable, withstand a wide range of temperatures, and tend to be more flexible and less 'brittle' than those made with PLA.
Acetone can be used post-process to provide a glossy look to your finished ABS product. ABS is best used with a heated bed as ABS contracts when cooled and large parts may pull off of a non-heated bed.
Features :
- ABS is dimensionally stable and impact resistant.
- It can also handle temperatures up to 85°C.
- making it well-suited for mechanical parts .
- 1.75mm filament diameter (Dimensional Accuracy +l- O.02mm)
- Vacuumed sealed with desiccunt and box packed.
- Printing temperature 220°C-250°C
- Bed temperature 100°C
- Available in wide range of colors
Specifications:
PROPERTIES |
STANDARD |
UNIT |
VALUES |
Rheological Properties |
|
|
|
Melt Flow
Index 220°C/10kg |
ISO 1133 |
Gms/10min |
18 |
Mould
Shrinkage |
D 955 |
% |
0.4-0.6 |
Thermal Properties |
|
|
|
Vicat
Softening Temperature |
D 1525 |
°C |
97 |
Heat
Deflection Temperature (annealed
80°C/4 hrs, 1.80mpa) |
D 648 |
°C |
93 |
Mechanical Properties |
|
|
|
RockWall
Hardness |
D 785 |
R-scale |
105 |
Tensile
Strength at Yield (50mm/min) |
D638 |
Kg/cm2 |
500 |
Tensile
Modulus (50mm/min) |
D638 |
Kg/cm2 |
27500 |
Flexural
Strength (5mm/min) |
D 790 |
Kg/cm2 |
700 |
Flexural
Modulus (5mm/min) |
D 790 |
Kg/cm2 |
24000 |
Izod Notched
Impact Strength (at
1/4" thickness) |
D 256 |
Kg-cm/cm |
20 |
Other Properties |
|
|
|